Hot & Cold work tool steels as per the Standard (A681) as well as customer requirement is produced based on design application, service condition and desired properties.

Typical Analysis In %

C Si Mn Cr W V Co Mo Ni
2 0.3 0.3 12 - - - - -


Heat Treatment & Processing

Forging Temp. °C Annealing Temp. °C Hardening Temp. °C Quenching Medium Tempering Temp. °C Hardness Rockwell °C
1050-850 800-850 920-980 O,CA,M 100-350 58-65


Equivalent Grades

BS 970 (REVISED) 1970-1972 BS 970-1955 En No. AISI/SAE DIN Japan U.S.S.R. IS
BD2* - D2 X165CrV12 - -
Grade Specification
XT160Cr12 3749/1978
Hot & Cold work tool steels as per the Standard (A681) as well as customer requirement is produced based on design application, service condition and desired properties.

Typical Analysis In %

C Si Mn Cr W V Co Mo Ni
1.7 0.3 0.3 12 0.5 0.1 - 0.6 -


Heat Treatment & Processing

Forging Temp. °C Annealing Temp. °C Hardening Temp. °C Quenching Medium Tempering Temp. °C Hardness Rockwell °C
1050-850 800-850 970-990 O,CA,M 100-350 58-65


Equivalent Grades

BS 970 (REVISED) 1970-1972 BS 970-1955 En No. AISI/SAE DIN Japan U.S.S.R. IS
BD 3* - D3 X165CrV12 - -
Grade Specification
XT215Cr12 4430/1979
Advanced practices for melting, hot working, and annealing have been developed which enable H-11 to be consistently supplied with a fine uniform annealed structure, as illustrated herein. This steel is readily heat treated to produce a uniformly fine grained microstructure. The structural uniformityresults in longer die life.

Typical Analysis In %

C Si Mn Cr W V Co Mo Ni
0.36 1 0.4 5 - 0.4 - 1.1 -


Heat Treatment & Processing

Forging Temp. °C Annealing Temp. °C Hardening Temp. °C Quenching Medium Tempering Temp. °C Hardness Rockwell °C
1100-900 800-830 980-1030 O,CA 550-650 38-52


Equivalent Grades

BS 970 (REVISED) 1970-1972 BS 970-1955 En No. AISI/SAE DIN Japan U.S.S.R. IS
BH 11* - H-11 38CrMoV51 - -
Grade Specification
XT35Cr5Mo1V3 3748/1978
Advanced practices for melting, hot working, and annealing have been developed which enable H-13 to be consistently supplied with a fine uniform annealed structure, as illustrated herein. This steel is readily heat treated to produce a uniformly fine grained microstructure. The structural uniformityresults in longer die life.

Typical Analysis In %

C Si Mn Cr W V Co Mo Ni
0.3 0.2 0.3 2.6 8.5 0.5 - - -


Heat Treatment & Processing

Forging Temp. °C Annealing Temp. °C Hardening Temp. °C Quenching Medium Tempering Temp. °C Hardness Rockwell °C
1100-900 740-780 1070-1150 O,CA,M 600-680 38-52


Equivalent Grades

BS 970 (REVISED) 1970-1972 BS 970-1955 En No. AISI/SAE DIN Japan U.S.S.R. IS
BH 13* - H-13 X40CrMoV51 - -
Grade Specification
XT35Cr5MoW1V1 3748/1978

About Us

We are pleased to introduce ourselves as a leading stockiest of Alloy Steel, Carbon Steel, Tool Steel, Die Steel, Mild Steel, & Bright Bars in each size and section.

We are today rated amongst the top stockiest and suppliers of Alloy steels & Forging steels in round and flats. Read More..

View On Maps

GUNJAN ALLOYS PVT.LTD.

70/2, Muncipal Plot,
Opp. Anil Estate, Ajod Dairy Road, Rakhial, Ahmedabad -23

079 22748600 | 079 22748700

079 22748800

info@gunjanalloys.com